Low alloy tool steel bar, mat number 1.3501
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-07-12 19:45
- Browse the number:
24
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.approvedenergyassessments.com/
Product details
Model Number: ZXL046
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steelApplicationsCan be used as structural steel for manufacturing of balls, rollers and needles for bearings up to 10mm of thicknessThis steel grade can be used also as tool steelChemical composition (in weight%)
C 1.00
Si 0.25
Mn 0.35
Cr 0.50
Ni 0.15
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.84
Soft annealing
Heat to 730-760℃, cool slowly
This will produce a maximum Brinell hardness of 207
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 600 to 650℃, holding for 1-2 hoursat heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 780 to 810℃, 820 to 850℃ followed by oil or water quenching
Hardness after quenching is about 60 HRC
Tempering
Tempering temperature: 150 to 180℃
Forging
Hot forming temperature: 1100 to 850℃
Specifications:
Grade: mat number 1.3501
Standards: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
C 1.00
Si 0.25
Mn 0.35
Cr 0.50
Ni 0.15
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.84
Soft annealing
Heat to 730-760℃, cool slowly
This will produce a maximum Brinell hardness of 207
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 600 to 650℃, holding for 1-2 hoursat heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 780 to 810℃, 820 to 850℃ followed by oil or water quenching
Hardness after quenching is about 60 HRC
Tempering
Tempering temperature: 150 to 180℃
Forging
Hot forming temperature: 1100 to 850℃
Specifications:
Grade: mat number 1.3501
Standards: DIN, GB
Diameter: 50-500mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Waterproof Slip Resistant Shoe Covers
price: Negotiable
-
Milk Products Packaging Bag
price: Negotiable
-
Front And Rear Mountable Flail Mower Mulcher
price: Negotiable
-
Cialis Tadalafil CAS 171596-29-5
price: Negotiable
-
T8 Tube Cover
price: Negotiable
-
Steel Structure Plant
price: Negotiable